Elaboration and characterizations of platinum nanoparticles supported on cellulose-based carbon aerogel - Archive ouverte HAL Accéder directement au contenu
Communication Dans Un Congrès Année : 2009

Elaboration and characterizations of platinum nanoparticles supported on cellulose-based carbon aerogel

(1) , (2) , (2) , (3) , (3) , (1) , (1)
1
2
3

Résumé

This work investigates the deposition of Pt nanoparticles onto carbon aerogels (CA), derived from microcrystalline cellulose. Nanoparticles are synthesised via impregnating the CA with H2PtCl6 followed by reduction either under H2 at 300 C or in a basic NaBH4 solution. H2 reduction yields uniform Pt nanoparticles (average diameter < 2nm) dispersed over the CA surface as revealed by Transmission electron microscopy (TEM). Larger agglomerates can be seen in TEM images of NaBH4 reduced samples, which is confirmed by powder X-ray diffraction (XRD). A rotating disk electrode was employed to analyse the electrochemical properties of the Pt nanoparticles. The active area of the platinum nanoparticles was evaluated using hydrogen adsorption/desorption cyclic voltammetry and CO stripping measurements. The oxygen reduction reaction was also studied to (i) obtain the kinetic parameters of oxygen reduction for the Pt/CA materials and (ii) compare them with commercial Pt/Carbon Black.
Fichier principal
Vignette du fichier
Joanna_Rooke_350.pdf (409.25 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00490263 , version 1 (16-06-2010)

Identifiants

  • HAL Id : hal-00490263 , version 1

Citer

Joanna Rooke, Claudia Hildenbrand, Sandrine Berthon-Fabry, Romain Sescousse, Tatiana Budtova, et al.. Elaboration and characterizations of platinum nanoparticles supported on cellulose-based carbon aerogel. International Carbon Conference 2009, Jun 2009, Biarritz, France. 6 p. ⟨hal-00490263⟩
400 Consultations
605 Téléchargements

Partager

Gmail Facebook Twitter LinkedIn More