Damage of semicrystalline polyamide 6 assessed by 3D X-ray tomography: From microstructural evolution to constitutive modeling
Abstract : In this study an attempt is made to link the damage and microstructural evolution of semicrystalline polymers, in particular polyamide 6, to the macroscopic material behavior during tensile and creep tests. Tensile specimens, removed before failure were seen to have undergone striction. They were examined using synchrotron radiation tomography. These samples showed elongated axisymmetric columns of voids separated by thin ligaments of material. These observations were confirmed and refined through a cryofractography experiment of a different tensile sample, stopped before failure. An attempt was made to obtain quantitative data about void volume fraction and morphology through image analysis.
Cited literature [32 references]
https://hal-mines-paristech.archives-ouvertes.fr/hal-00509794
Contributor : Bibliothèque Umr7633 Connect in order to contact the contributor
Submitted on : Thursday, July 12, 2018 - 11:26:52 AM
Last modification on : Wednesday, November 17, 2021 - 12:28:29 PM
Long-term archiving on: : Monday, October 15, 2018 - 10:42:20 PM
Contributor : Bibliothèque Umr7633 Connect in order to contact the contributor
Submitted on : Thursday, July 12, 2018 - 11:26:52 AM
Last modification on : Wednesday, November 17, 2021 - 12:28:29 PM
Long-term archiving on: : Monday, October 15, 2018 - 10:42:20 PM
File
Laiarinandrasana-Morgeneyer J....
Publisher files allowed on an open archive