Shear-induced crystallization of polypropylenes: effect of molecular weight

Abstract : The crystallization kinetics of three polypropylenes with different molecular weights was studied during shear under isothermal condition with a fibre pull-out device. Nucleation and growth under shear were observed and compared to static conditions. The crystalline growth rate was measured both in static condition and under shear. In static condition, the morphologies are α-phase spherulites and are formed from nuclei which are randomly distributed. Under shear α-phase morphologies are still observed but the nucleation density and the growth rate depend on the shear-rate. The nucleation density is strongly enhanced by shear and acts as the main factor on the overall kinetics. The growth rate increases with the shear-rate, but the basic growth mechanisms seem to be unmodified. β phase appears after shear during the relaxation of the orientation
Document type :
Journal articles
Complete list of metadata

https://hal-mines-paristech.archives-ouvertes.fr/hal-00574876
Contributor : Magalie Prudon <>
Submitted on : Wednesday, March 9, 2011 - 9:20:27 AM
Last modification on : Thursday, September 24, 2020 - 5:22:55 PM

Links full text

Identifiers

Citation

Frederic Jay, Jean-Marc Haudin, Bernard Monasse. Shear-induced crystallization of polypropylenes: effect of molecular weight. Journal of Materials Science, Springer Verlag, 1999, 34 (9), pp.Pages 2089-2102. ⟨10.1023/A:1004563827491⟩. ⟨hal-00574876⟩

Share

Metrics

Record views

175