Characterisation of the dilatational stress relaxation for viscoelastic Polyurethane materials

Abstract : This contribution deals with three grades of polyurethane (PU) devoted to ensure sealing of filter cartridge endplate. PU is an amorphous polymer whose microstructure depends on the supplier processing. During service, the endplates are submitted to complex thermo-mechanical loading consisting of an applied pressure with a continuous increase of the temperature. The inner diametrical dilatation is the key parameter that has to be controlled. The main loading deals then with transient thermal expansion as well as hydrostatic pressure.
Type de document :
Communication dans un congrès
Liste complète des métadonnées

https://hal-mines-paristech.archives-ouvertes.fr/hal-00579510
Contributeur : Magalie Prudon <>
Soumis le : jeudi 24 mars 2011 - 10:16:06
Dernière modification le : jeudi 24 septembre 2020 - 18:30:07
Archivage à long terme le : : jeudi 8 novembre 2012 - 12:26:15

Fichier

epjconf_ICEM14_03004.pdf
Fichiers éditeurs autorisés sur une archive ouverte

Identifiants

Citation

Angélique Consil, Noëlle Billon, Lucien Laiarinandrasana. Characterisation of the dilatational stress relaxation for viscoelastic Polyurethane materials. 14th International Conference on Experimental Mechanics (ICEM 14), Jul 2010, Poitiers, France. Article Number 03004 - 2 p., ⟨10.1051/epjconf/20100603004⟩. ⟨hal-00579510⟩

Partager

Métriques

Consultations de la notice

324

Téléchargements de fichiers

356