Thermal fatigue failure of brass die-casting dies

Abstract : This research has been conducted to elucidate the mechanisms of brass die casting failure. A die was examined and we have evaluated the causes of crack failure mechanisms after use in brass die casting. The dominating failure mechanism in the investigated die was thermal fatigue cracking. Crack initiation is associated to accumulation of the local plastic strain that occurs during each casting cycle. The crack growth is facilitated by a number of elements: oxidation of the cracks' surfaces, filling of brass and softening of the die material.
Type de document :
Article dans une revue
Liste complète des métadonnées

https://hal-mines-paristech.archives-ouvertes.fr/hal-00675703
Contributeur : Bibliothèque Umr7633 <>
Soumis le : jeudi 1 mars 2012 - 17:21:35
Dernière modification le : mercredi 7 octobre 2020 - 16:36:06

Identifiants

Citation

Dhouha Mellouli, Nader Haddar, Alain Köster, Hassine Ferid Ayedi. Thermal fatigue failure of brass die-casting dies. Engineering Failure Analysis, Elsevier, 2012, 20, pp.137-146. ⟨10.1016/j.engfailanal.2011.11.006⟩. ⟨hal-00675703⟩

Partager

Métriques

Consultations de la notice

391