A functionally graded multilayer approach to the synthesis of boron containing ceramic thin films - Mines Paris Accéder directement au contenu
Article Dans Une Revue Solid State Sciences Année : 2012

A functionally graded multilayer approach to the synthesis of boron containing ceramic thin films

O. Addemir
  • Fonction : Auteur
O. Yucel
  • Fonction : Auteur

Résumé

Despite their excellent properties, adhesion problems are common for B4C and BCN thin films on different substrates when the film thickness exceeds about 500 nm. Three functionally graded multilayer designs; surface boronizing of the steel substrate before deposition (Boride underlayer/B4C), Ti/TiC/B4C and Ti/TiN/BCN structures were discussed in this study, to alleviate the adhesion problems. Cross-sectional FE-SEM examinations and elemental depth profiling by SIMS revealed the graded structure of the films. The elemental film composition measured by EPMA and the mechanical properties determined by nanoindentation demonstrated the graded chemical composition and the transition of the hardness and Young's modulus values between different layers respectively. The results demonstrated the possibility of growing well adherent boron containing ceramic coatings with thicknesses in the μm range by means of different graded underlayer designs.

Domaines

Matériaux

Dates et versions

hal-00765531 , version 1 (14-12-2012)

Identifiants

Citer

Tolga Tavsanoglu, O. Addemir, Michel Jeandin, O. Yucel. A functionally graded multilayer approach to the synthesis of boron containing ceramic thin films. Solid State Sciences, 2012, 14, pp.1717-1721. ⟨10.1016/j.solidstatesciences.2012.06.014⟩. ⟨hal-00765531⟩
133 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More