Characterization and modeling of ductile rupture with relationship to microstructures in 2198 Al-Li alloy for aeronautic application

Abstract : Damage and fracture mechanisms of two 2198 Al-Li thin sheet alloys having different thicknesses (2 and 6 mm) are investigated. Two heat treatments are studied: T3 and T8. Mechanical tests are carried out on flat specimens including smooth tensile samples and U-notched specimens (with various notch radii). Test data are used to identify the parameters of constitutive equations describing plastic anisotropy. Crack initiation and stable propagation is studied using Kahn tear tests. The microscopic fracture surface of the different specimens is observed using SEM (Scanning Electron Microscopy). Smooth and notched samples exhibit a slant fracture surface. With increasing notch severity, the fracture mode changes significantly. Failure initiates at the notch root in a small triangular region, outside this zone, slant fracture is observed. Observations show two different failure mechanisms with respect to triangular and slant zones.
Type de document :
Communication dans un congrès
Liste complète des métadonnées

Littérature citée [6 références]  Voir  Masquer  Télécharger

https://hal-mines-paristech.archives-ouvertes.fr/hal-00822292
Contributeur : Bibliothèque Umr7633 <>
Soumis le : mardi 14 mai 2013 - 14:08:53
Dernière modification le : jeudi 24 septembre 2020 - 18:30:04
Archivage à long terme le : : mardi 4 avril 2017 - 06:58:18

Fichier

Chen-Besson-Madi_ICF_12_Ottawa...
Fichiers éditeurs autorisés sur une archive ouverte

Identifiants

  • HAL Id : hal-00822292, version 1

Citation

Jianqiang Chen, Jacques Besson, Yazid Madi. Characterization and modeling of ductile rupture with relationship to microstructures in 2198 Al-Li alloy for aeronautic application. International conference on fracture, Jul 2009, Ottawa, Canada. 10 p. ⟨hal-00822292⟩

Partager

Métriques

Consultations de la notice

280

Téléchargements de fichiers

172