Phase selection and microstructure formation in undercooled Co-61.8 at.% Si melts under various containerless processing conditions

Abstract : The hypoeutectic composition Co-61.8 at.% Si was undercooled and solidified using electromagnetic levitation, electromagnetic levitation under a static magnetic field, electrostatic levitation and glass-fluxing. The samples generally showed two thermal events, either separated or continuous depending on undercooling. In situ monitoring of the two thermal events with a high-speed camera revealed a sudden decrease of dendritic growth velocities of primary phases at a critical undercooling of 88 K. Scanning electron microscopy studies of the solidified samples showed that the CoSi compound and the CoSi2 compound nucleate as the primary phase for low and high undercoolings, respectively. The microstructure of the samples depends not only on undercooling, but also on the onset temperature or delay time of the second thermal event. Melt convection has no effect on the primary phase selection in undercooled melts, but it has a significant effect on the delay time and therefore on microstructure formation of the samples for high undercoolings
Type de document :
Article dans une revue
Liste complète des métadonnées

https://hal-mines-paristech.archives-ouvertes.fr/hal-00834066
Contributeur : Magalie Prudon <>
Soumis le : vendredi 14 juin 2013 - 10:00:08
Dernière modification le : jeudi 17 septembre 2020 - 12:28:40

Identifiants

Citation

Yong K Zhang, Jianrong Gao, Matthias Kolbe, S. Klein, Chunzheng Yang, et al.. Phase selection and microstructure formation in undercooled Co-61.8 at.% Si melts under various containerless processing conditions. Acta Materialia, Elsevier, 2013, 61 (13), pp.4861-4873. ⟨10.1016/j.actamat.2013.04.061⟩. ⟨hal-00834066⟩

Partager

Métriques

Consultations de la notice

365