A local approach to creep-fatigue-oxidation interactions in Inco 718 alloy

Abstract : Understanding and modeling hold time effects on fatigue crack growth rate (FCGR) above 500 °C in Inco 718DA is a great challenge. Fatigue tests with a trapezoidal wave shape signal including hold times from 90 s to 3600 s were carried out on Inco 718DA with a small grain size (5-15 μm) over a wide range of temperatures (500 °C-650 °C). FCGRs were measured using potential drop technique. SEM observations were carried out to correlate the measured FCGRs with the trans- or inter-granular aspect of the fatigue fracture surfaces. Two regimes must be distinguished. The first regime associated with relatively short hold times can be represented by a power law, where da/dN is proportional to tα, α ~ 0.25. This first regime corresponds to the situation where the fatigue crack does not propagate during the hold time but its propagation takes place during the cyclic part of the loading over a damaged zone ahead of the crack tip. The second regime associated with longer hold times corresponds to the case where crack propagation during hold time (creep crack growth) is predominant. This regime is purely time dependent. Simple models are introduced to describe both regimes.
Type de document :
Communication dans un congrès
Liste complète des métadonnées

Littérature citée [27 références]  Voir  Masquer  Télécharger

https://hal-mines-paristech.archives-ouvertes.fr/hal-00853420
Contributeur : Bibliothèque Umr7633 <>
Soumis le : jeudi 14 novembre 2013 - 16:15:08
Dernière modification le : mercredi 14 octobre 2020 - 03:52:48
Archivage à long terme le : : samedi 15 février 2014 - 04:28:57

Fichier

Pineau-Moura_Pinho_ICF_13_Beij...
Fichiers éditeurs autorisés sur une archive ouverte

Identifiants

  • HAL Id : hal-00853420, version 1

Citation

André Pineau, Raul de Moura Pinho, Stéphane Pierret, Caroline Mary. A local approach to creep-fatigue-oxidation interactions in Inco 718 alloy. 13th international conference on fracture, Jun 2013, Beijing, China. 11 p. ⟨hal-00853420⟩

Partager

Métriques

Consultations de la notice

545

Téléchargements de fichiers

459