Failure of magnesium sheets under monotonic loading : 3D examination of fracture mode and mechanisms

Abstract : Damage evolution in a commercial magnesium sheet alloy (Mg-3Al-1Zn-0.3Mn) at room temperature is investigated. Kahn tear tests were performed to characterize the crack extension behaviour. Scanning electron microscopy of the fracture surfaces revealed flat inclined areas and the absence of cracked particles and dimples. Post-mortem synchrotron tomography of a stopped crack was used to further identify the predominant damage mechanism in the specimen's ligament. Nucleation of submicrometre-voids, a micro-void sheeting mechanism and the absence of classical void growth could be identified.
Type de document :
Article dans une revue
Liste complète des métadonnées

https://hal-mines-paristech.archives-ouvertes.fr/hal-00869572
Contributeur : Bibliothèque Umr7633 <>
Soumis le : jeudi 3 octobre 2013 - 16:28:18
Dernière modification le : jeudi 24 septembre 2020 - 18:30:07

Lien texte intégral

Identifiants

Citation

D. Steglich, Thilo F. Morgeneyer. Failure of magnesium sheets under monotonic loading : 3D examination of fracture mode and mechanisms. International Journal of Fracture, Springer Verlag, 2013, 183, pp.105-112. ⟨10.1007/s10704-013-9863-y⟩. ⟨hal-00869572⟩

Partager

Métriques

Consultations de la notice

190