Direct grafting of ethylene sulfide onto silicic acid magadiite

Abstract : Acidic magadiite (HMag) was directly reacted with ethylene sulfide (ES) under various controlled conditions producing an intercalated hybrid silicate (MagS). The sodium, acidic and modified magadiites were characterized using elemental analysis, thermogravimetric analysis (TGA/DTG), infrared spectroscopy, 13C and 29Si NMR spectroscopies, scanning electronic microscopy and energy dispersive spectrometer. The modified solids were used to retain lead found in aqueous solutions. The results showed that ethylene sulfide was grafted as a dimer in the interlayer space of HMag, which was concluded from the XRD experiments due to an increase in the basal spacing from 1.34 to 1.81 nm. This was in agreement with the high sulfur content obtained by elemental analysis. A higher amount of ethylene sulfide was immobilized in the layered material without the use of a solvent. The adsorption of lead revealed the formation of interlayer complexes involving the cation and the mercapto chelating groups. The method described herein provides a simple route for the synthesis of inorganic-organic magadiite.
Type de document :
Article dans une revue
Liste complète des métadonnées

https://hal-mines-paristech.archives-ouvertes.fr/hal-01018650
Contributeur : Bibliothèque Umr7633 <>
Soumis le : vendredi 4 juillet 2014 - 15:54:08
Dernière modification le : samedi 3 octobre 2020 - 04:19:59

Identifiants

Citation

Michelle Menezes de Oliveira, Marcia Maria Fernandes, Maria Gardennia Fonseca, Edson Cavalcanti da Silva Filho, Antonio Gouveia de Souza, et al.. Direct grafting of ethylene sulfide onto silicic acid magadiite. Microporous and Mesoporous Materials, Elsevier, 2014, 196, pp.292-299. ⟨10.1016/j.micromeso.2014.05.010⟩. ⟨hal-01018650⟩

Partager

Métriques

Consultations de la notice

1460