Impression et recuit de nanoparticules métalliques pour l’électronique imprimée
Résumé
The recent progress in functionalized inks based on metal nanoparticles and their subsequent deposition by inkjet-printing technologies promoted the emergence of printed electronics. Such printed structures can be treated by selective sintering techniques that enable the sintering of 20 nm-nanoparticles at process temperatures compatible with flexible plastic substrates. This article discusses the various aspects related to the production of metal tracks on flexible substrates, from the deposition using direct printing technologies, to the relationship between microstructural characteristics and electrical properties of such structures for the fabrication of devices such as antennas, interconnects
or electrodes.
Le développement récent d’encres fonctionnalisées constituées de nanoparticules métalliques, associé à la maîtrise du procédé d’impression par jet d’encre, a rendu possible l’émergence de l’électronique imprimée. Les structures imprimées peuvent être traitées par des techniques de recuit sélectif qui permettent de réaliser la coalescence de nanoparticules de 20 nm à une température de procédé compatible avec les substrats plastiques flexibles. Cet article aborde les différents aspects liés à la réalisation de pistes métalliques sur substrat souple, depuis les technologies d’impression directes, jusqu’à l’adéquation entre les caractéristiques microstructurales et les propriétés électriques de telles structures pour la fabrication de dispositifs tels que des antennes, des pistes de routage ou des électrodes.