In situ observation of strained bands and ductile damage in thin AA2139-T3 alloy sheets

Résumé

The interactions between plasticity and damage mechanisms are not clearly established concerning the fracture of ductile sheet materials (e.g., flat to slant transition). The question addressed herein is to elucidate which mechanism is responsible for localized phenomena leading to the final failure. A mechanical test carried out on a notched plate made of 2139-T3 aluminum alloy is imaged thanks to synchrotron laminography at micrometer resolution. Ductile damage (i.e., void nucleation, growth and coalescence) is analyzed via reconstructed volumes. Although the low volume fraction of secondary phases in the tested alloy is challenging, digital volume correlation is also utilized to measure displacement fields and estimate strain fields in the bulk of the alloy during the whole test. In the first part of this study, the resolution of the measurement technique is assessed under such conditions. Then strained bands are shown to occur very early on in what will be the slant region of the fracture path. Conversely, damage grows at very late loading steps.
Fichier principal
Vignette du fichier
Buljac-Taillandier-Morgeneyer Procedia IUTAM 2017 66-72.pdf (481.98 Ko) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-01518925 , version 1 (05-05-2017)

Identifiants

Citer

Ante F Buljac, Thibault F Taillandier-Thomas, Thilo F. Morgeneyer, Lukas F Helfen, Stéphane Roux, et al.. In situ observation of strained bands and ductile damage in thin AA2139-T3 alloy sheets. Procedia IUTAM, 2017, 20, pp.66-72. ⟨10.1016/j.piutam.2017.03.009⟩. ⟨hal-01518925⟩
346 Consultations
152 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More