Processing and properties of sorghum stem fragment-polyethylene composites

Thi To Loan Vo (1) , Jordi Girones (1) , Calypso Beloli (1) , Lucie Chupin (1) , Erika Di Giuseppe (1) , Anne Clément-Vidal (2) , Armelle Soutiras (2) , David Pot (2) , Denis Bastianelli (3) , Laurent Bonnal (3) , Patrick Navard (1)

1 CEMEF - Centre de Mise en Forme des Matériaux
2 UMR AGAP - Amélioration génétique et adaptation des plantes méditerranéennes et tropicales
3 UMR SELMET - Systèmes d'élevage méditerranéens et tropicaux

Composites prepared with whole sorghum stem fragments reinforcing a polyethylene matrix were studied using ten different sorghum genotypes. Using a robust processing protocol, it is shown that for a given sorghum genotype, the composition of the stem fragments varies depending on the size of the sieved fragments but with the genotype effect being larger than the sieving effect. There is a variation of mechanical properties between the genotypes (from 0.6 to 1 GPa for modulus, from 7.2 to 11.5 MPa for tensile strength and from 4.4 to 6.2 kJ/m2 for impact strength). The genotypes giving the best tensile mechanical properties are the ones which have the highest viscosity, which show during blending the largest energy dissipation and which have the less decrease of size after processing. There is a weak correlation between tensile mechanical properties and resistance to impact suggesting that it is not the same tissues or physical properties which contribute to these two tests.

Mots clés: Sorghum; Mechanical properties; Injection molding; Biocomposites

Domaines: Matériaux

Thi To Loan Vo, Jordi Girones, Calypso Beloli, Lucie Chupin, Erika Di Giuseppe, et al.. Processing and properties of sorghum stem fragment-polyethylene composites. Industrial Crops and Products, 2017, 107, pp.386 - 398. ⟨10.1016/j.indcrop.2017.05.047⟩. ⟨hal-01541489⟩