Influence of the dislocation density on hardening precipitation in Inconel© 625

(1) , (1) , (1) , (2) , (1)
1
2
Marc Bernacki
Jonathan Cormier
  • Fonction : Auteur
  • PersonId : 998670

Résumé

Inconel© 625 is a Nickel-base superalloy used in aerospace industry as turbine shrouds, spray bars, hydraulic tubing, armoring and thrust reversers systems [1]. One reason of its use is its high mechanical properties at high temperature. Inconel© 625 is strengthened by precipitation of γ″ phase, tetragonal Ni 3 Nb [1]. Since dislocations can influence precipitation [2], the precipitation of γ″ in Inconel© 625 was studied in samples submitted to cold straining to induce different dislocation contents before precipitation heat treatment.

Mots clés

Fichier principal
Vignette du fichier
JA2017_0033.pdf (258.69 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01624670 , version 1 (26-10-2017)

Identifiants

  • HAL Id : hal-01624670 , version 1

Citer

Anthony Seret, Charbel Moussa, Marc Bernacki, Jonathan Cormier, Nathalie Bozzolo. Influence of the dislocation density on hardening precipitation in Inconel© 625. Journées annuelles SF2M, SF2M (Société Française de Métallurgie et des Matériaux), Oct 2017, Lyon, France. ⟨hal-01624670⟩
286 Consultations
217 Téléchargements

Partager

Gmail Facebook Twitter LinkedIn More