On the crystallographic, stage I-like, character of fine granular area formation in internal fish-eye fatigue cracks

Abstract : The crystallographic character of fine granular area (FGA) formation from internal particles in martensitic high strength steel has been revealed by an assessment of the plastic zone size at the FGA border. This plastic zone size corresponded to about 3 times the martensite lath width. Tests at different temperatures (20 °C, 200 °C and 400 °C) revealed a decreasing FGA size with increasing temperature at constant applied stress amplitude. As a consequence, the critical stress intensity factor varied as the FGA decreased with temperature. In contrast, the critical plastic zone size remained constant and equal to the sizes of microstructural features. This represents a strong similarity between crystallographic, stage I-like, crack propagation and FGA formation in a vacuum.
Type de document :
Article dans une revue
Liste complète des métadonnées

Littérature citée [33 références]  Voir  Masquer  Télécharger

https://hal-mines-paristech.archives-ouvertes.fr/hal-01633714
Contributeur : Bibliothèque Umr7633 <>
Soumis le : mercredi 22 janvier 2020 - 15:06:34
Dernière modification le : jeudi 9 avril 2020 - 17:08:06
Document(s) archivé(s) le : jeudi 23 avril 2020 - 15:34:24

Fichier

Abdesselam_etal_2018.pdf
Fichiers produits par l'(les) auteur(s)

Identifiants

Citation

Hayat Abdesselam, Jérôme Crépin, André Pineau, Anne-Laure Rouffié, P. Gaborit, et al.. On the crystallographic, stage I-like, character of fine granular area formation in internal fish-eye fatigue cracks. International Journal of Fatigue, Elsevier, 2018, 106, pp.132-142. ⟨10.1016/j.ijfatigue.2017.09.013⟩. ⟨hal-01633714⟩

Partager

Métriques

Consultations de la notice

278

Téléchargements de fichiers

97