Microstructure and mechanical properties of a nanocomposite oxide system : the Nextel 720 fibre

Abstract : The two phase microstructure and the mechanical properties of the 3M Nextel 720 fibre annealed at different temperatures were investigated. The as received fibre was found to be composed of pseudo-tetragonal mullite aggregates enclosing elongated or round shaped α-alumina grains. After annealing the fibre at 1400°C the mullite structure became orthorhombic while losing alumina. A small increase of the Young modulus was observed because of the change of relative amounts of alumina and mullite and a diminution of the porosity. Thanks to its original microstructure the fibre was found to have a reduced creep rate when compared to other polycristalline oxide fibres but it was found to be extremely sensitive to external conditions and to suffer from premature failure due to slow crack growth (SCG).
Type de document :
Communication dans un congrès
Liste complète des métadonnées

Littérature citée [14 références]  Voir  Masquer  Télécharger

https://hal-mines-paristech.archives-ouvertes.fr/hal-01843197
Contributeur : Bibliothèque Umr7633 <>
Soumis le : mercredi 18 juillet 2018 - 16:01:34
Dernière modification le : lundi 12 novembre 2018 - 10:59:14
Document(s) archivé(s) le : vendredi 19 octobre 2018 - 23:08:35

Fichier

Deléglise-Berger-Bunsell ICCM...
Fichiers produits par l'(les) auteur(s)

Identifiants

  • HAL Id : hal-01843197, version 1

Citation

Florence Deleglise, Marie-Hélène Berger, Anthony R. Bunsell. Microstructure and mechanical properties of a nanocomposite oxide system : the Nextel 720 fibre. ICCM 12, Jun 1999, Paris, France. 10 p. ⟨hal-01843197⟩

Partager

Métriques

Consultations de la notice

342

Téléchargements de fichiers

18